| TUBALOY 23 |
HARDNESS
(as deposited) : 58-60 RC
(multilayer) : 62-64 RC
Size (mm) : 6.00 8.00 11.00
Current (amps) : 80-125 140-190 190-250
|
A special alloy consists of hard austenitic matrix with carbides of chromium, niobium, molybdnum, tungsten and vanadium.
This is designed for resistance to severe abrasion and erosion at both ambient and elevated
temperatures (up to 800 º C). Used for sinter fans,
sinter breakers, blast furnace bells and hoppers, cement kiln, wear plates, clinker wear plates.
|
|
| TUBALOY 33 |
HARDNESS : 50-55 Rc
(Multi Layer) : 56-60 Rc
Size (mm) : 6.00 8.00 11.00
Current (amps) : 80-125 140-190 190-250
|
An austenitic iron type of tubular electrode designed for welding of manganese steels to obtain
a very abrasion resistant and impact resistant surface.
It is also used for hardfacing on carbon and low alloy steels.
Applications include crusher hammers, mantles and liners bucket lips and teeth, blow bars etc.
|
|
| TUBALOY 35 |
HARDNESS
(Single layer) : 50-60 Rc
(Multilayer) : 58-62 Rc
Size (mm) : 6.00 8.00 11.00
Current (amps) : 80-125 140-190 190-250
|
An austenitic iron type of tubular electrode having tough austenitic matrix
with large quantities of chromium and molybdenum carbides.
Deposit resists grinding abrasion. Can be applied directly
on grey cast iron and low carbon steels without preheating. Suitable
for crushing equipments, earthmoving and agricultural machineries.
|
|
| TUBALOY108 |
HARDNESS
(as deposited) : 15 - 20 Rc
(Work hardened) : 45-48 Rc
Size (mm) : 6.00 8.00 11.00
Current (amps) : 80-125 140-190 190-250
|
A chrome-manganese type of tubular electrode having vanadium as alloy
constituent. Deposit work- hardens rapidly and gives resistance
to both abrasion and impact.
Applications include crusher mantles, hammers, blow bars etc.
|
|